Manchamento do tecido dental promovido por diferentes fases de um cimento de aluminato de cálcio

Abstract

RESUMO

Este estudo avaliou o manchamento de dentes tratados com diferentes fases do cimento de aluminato de cálcio (CAC), comparativamente ao CAC convencional ao MTA. Foram utilizados 50 incisivos bovinos que, após preparo e obturação dos canais radiculares, tiveram 2 mm de sua obturação removida para confecção de um plug cervical. Assim dentes foram distribuídos (n=10) de acordo com o material utilizado para confecção do Plug cervical: - cimento experimental obtido a partir das diferentes fases do CAC - CA (CaO.Al2O3) (G1), CA2 (CaO.2Al2O3) (G2), C12A7 (12CaO.7Al2O3) (G3); CAC convencional (G4) e MTA (G5). Foi realizada leitura de cor inicial (baseline) com dispositivo de mensuração intraoral (Easyshade, VITA) na face vestibular dos dentes posicionados sobre fundo branco absoluto. Após 7, 15, 30, 45, 90, 120 e 180 dias, novas leituras de cor foram realizadas para determinar a diferença de cor (ΔE00), luminosidade (ΔL’), croma (ΔC’) e matiz (ΔH’). ΔE00 foi calculada entre os grupos e tempos segundo sistema CIEDE2000, e analisada estatisticamente por ANOVA. ΔL’, ΔC’ e ΔH’ foram analisadas pelos testes ANOVA de medidas repetidas e Tukey (p<0,05). ΔE00 não se mostrou significante entre os grupos testados (p=0,05); porém, quando os tempos foram comparados com o baseline, diferença significativa na ordem de 3,52 (G1-45 dias), 4,37(G2-45 dias), 4,45 (G2-30 dias), 3,54 (G4-120 dias) e 5,25 (G5-120 dias) foi observada (p=0,025). Diferença de croma foi significativa entre os grupos testados (p<0,001). A luminosidade diminuiu em todos os grupos e nos tempos testados (p=0,025). Todos os cimentos alteraram os padrões colorimétricos com o passar do tempo, em especial a luminosidade dental.

Palavras-Chaves: cimento de aluminato de cálcio; mineral trióxido agregado; alteração de cor.

ABSTRACT

The purpose of this study was to evaluate the staining of teeth treated with different phases of calcium aluminate cement (CAC), in comparison with conventional CAC and MTA. Fifty bovine incisors were used. After root canal preparation and obturation, 2 mm of the filling material was removed to cervical plug fabrication. The teeth were then distributed (n=10) according to the material used for cervical plug fabrication, as follows: - experimental cement obtained from the different phases of CAC - CA (CaO.Al2O3) (G1), CA2 (CaO2Al2O3) (G2), C12A7 (12CaO.7Al2O3) (G3); Conventional CAC (G4) and MTA (G5). Baseline reading was performed with an intraoral measuring device (Easyshade, VITA) on the buccal surface of the teeth positioned on an absolute white background. After 7, 15, 30, 45, 90, 120, and 180 days, new color readings were taken to determine the color difference (ΔE00), luminosity (ΔL’), chroma (ΔC’), and hue (ΔH’). ΔE00 was calculated among groups and times according to the CIEDE2000 system, and statistically analyzed by ANOVA. ΔL’, ΔC’ and ΔH ’were analyzed by ANOVA repeated measures and Tukey test (p<0.05). ΔE00 was not significant among the tested groups (p=0.05); However, when the times were compared with the baseline, a significant difference in the order of 3.52 (G1-45 days), 4.37 (G2-45 days), 4.45 (G2-30 days), 3.54 (G4-120 days) and 5.25 (G5-120 days) was observed (p=0.025). Chroma difference was significant among the tested groups (p<0.001). The luminosity decreased in all groups and tested times (p=0.025). All cements changed the colorimetric patterns over the course of time, especially the tooth luminosity.

Keywords: Calcium Aluminate Cement; Mineral Aggregate Trioxide; Color change.