Estudo de envelhecimento termo-oxidativo de gaxetas de permutadores de calor provenientes da indústria petroquímica

Repositório institucional da UFSC

A- A A+

Estudo de envelhecimento termo-oxidativo de gaxetas de permutadores de calor provenientes da indústria petroquímica

Mostrar registro simples

dc.contributor Universidade Federal de Santa Catarina. pt_BR
dc.contributor.advisor Dutra, Gabriel Benedet
dc.contributor.author Ruijter, Pedro Quirinus de
dc.date.accessioned 2022-12-21T00:08:39Z
dc.date.available 2022-12-21T00:08:39Z
dc.date.issued 2022-12-16
dc.identifier.uri https://repositorio.ufsc.br/handle/123456789/243288
dc.description TCC (graduação) - Universidade Federal de Santa Catarina, Campus Joinville, Engenharia Naval. pt_BR
dc.description.abstract Gaxetas elastoméricas são amplamente utilizadas na indústria petroquímica como elementos de vedação. Estes materiais são expostos em diferentes condições de temperatura e meio. Devido a essa variabilidade de operação, há uma imprevisibilidade do tempo de vida útil de gaxetas e da evolução de suas propriedades. Com isso, realizou-se o envelhecimento termo-oxidativo de gaxetas de HNBR e NBR em períodos de até 60 dias a 80, 95, 110, 140 e 170 °C. As propriedades avaliadas de Compression Set (CS), dureza e densidade de ligações cruzadas demonstraram taxas de degradação superiores para os corpos de prova de NBR. Com a análise de perfil de módulo de indentação, evidenciou-se a degradação heterogênea para HNBR (a 170 °C) e para NBR (a 140 e 170 °C), constatando o efeito DLO responsável por alterar a taxa de degradação das propriedades. Por último, a previsão de vida útil para o intervalo de temperaturas analisado, com a utilização dos métodos de TTS e Arrhenius por meio das curvas de evolução de CS sem o efeito DLO, demonstrou que as gaxetas de HNBR apresentam tempo de vida útil superior em relação às de NBR, comprovando maior resistência ao envelhecimento termo-oxidativo para o elastômero hidrogenado. pt_BR
dc.description.abstract Elastomeric gaskets are widely used in the petrochemical industry as sealing elements. Those materials are exposed to different conditions of temperature and environment. Due to this variability of operation, there is an unpredictability of the useful lifetime of gaskets and the evolution of their properties. With this, the thermo-oxidative aging of gaskets of HNBR and NBR was conducted in periods up to 60 days at 80, 95, 110, 140 and 170 °C. The evaluated properties of Compression Set (CS), hardness and cross-link density demonstrated superior degradation rates for the NBR specimens. With the analysis of the indentation modulus profile, heterogeneous degradation was evidenced for HNBR (at 170 °C) and for NBR (at 140 and 170 °C), verifying the DLO effect responsible for changing the degradation rate of the properties. Finally, the service lifetime prediction for the analyzed temperature range, using the TTS and Arrhenius methods through the CS evolution curves without the DLO effect, demonstrated that the HNBR gaskets have superior service lifetime to those of NBR, proving the superior resistance to thermos-oxidative ageing for the hydrogenated elastomer. pt_BR
dc.format.extent 46 f. pt_BR
dc.language.iso pt_BR pt_BR
dc.publisher Joinville, SC. pt_BR
dc.rights Open Access. en
dc.subject NBR pt_BR
dc.subject HNBR pt_BR
dc.subject Envelhecimento termo-oxidativo pt_BR
dc.subject Previsão de tempo de vida pt_BR
dc.subject DLO pt_BR
dc.title Estudo de envelhecimento termo-oxidativo de gaxetas de permutadores de calor provenientes da indústria petroquímica pt_BR
dc.type TCCgrad pt_BR


Arquivos deste item

Arquivos Tamanho Formato Visualização Descrição
TCC - Pedro Quirinus de Ruijter.pdf 766.7Kb PDF Visualizar/Abrir TCC - Pedro Quirinus de Ruijter

Este item aparece na(s) seguinte(s) coleção(s)

Mostrar registro simples

Buscar DSpace


Busca avançada

Navegar

Minha conta

Estatística

Compartilhar